MA-X
Ni-22Cr-18Fe-9Mo-1.5Co-0.6W (mass%)
Nickel alloy that has excellent strength, oxidation resistance and formability at high temperature
Main Features
The strength and oxidation resistance of MA-X proves to be good at temperatures up to 1200°C. It also has excellent formability and weldability. Since MA-X has excellent resistance to oxidizing, reducing and neutral atmospheres, its utilization in heating furnace parts manufacturing is particularly recommended. MA-X also is the most suitable material for jet engine tail pipes, afterburners , nozzle vein, cabin heaters, and other aircraft components.
Weldability/Workability
Plastic deformation is possible with MA-X. In addition, due to its good weldability, general welding with inert gas coating arc (TIG and MIG)is possible. Resistance welding can be used as well.
Heat Treatment
Wrought forms of MA-X alloy are furnished in the solution heat-treated condition unless otherwise specified. MA-X alloy is solution heat-treated and rapid cooled.
Available Product Forms
Various shapes, such as flat-rolled plates, forgings, welding wires, wires, welded pipes and tubes, seamless pipes and tubes can be manufactured.
Specifications
Information on specifications to which MA-X alloy can be ordered.
ASTM UNS N06002
| Plates | Bars, Forgings | Pipes and Tubes | Joints |
|---|---|---|---|
| B435 | B572 | B619 | B366 |
| B622 | |||
| B626 |
ASME UNS N06002
| Plates | Bars, Forgings | Pipes and Tubes | Joints |
|---|---|---|---|
| SB-435 | SB-572 | SB-619 | SB-366 |
| SB-622 | - | ||
| SB-626 |
JIS NW6002
| Plates | Bars | Pipes and Tubes | Wires |
|---|---|---|---|
| H4551 | H4553 | H4552 | H4554 |
AMS UNS N06002
| Plates | Bars, Forgings | Pipes and Tubes |
|---|---|---|
| 5536 | 5754 | 5587 5588 |